TPE DuraGrip® DGR 6070NC USA Advanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒 | ISO 868 | 68 |
| 邵氏A,5秒 | ASTM D2240 | 68 |
| Mechanical properties | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| Taber wear resistance | 1000Cycles,1.0E+6g,CS-17Wheel | ASTM D1044 | 10.0 mg |
| physical property | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| Shrinkage rate | TD：3.18mm | ASTM D955 | 1.2 % |
| TD:1.59mm | ISO 294-4 | 1.1 % | |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 104 Pa·s |
| Shrinkage rate | MD：1.59mm | ASTM D955 | 2.1 % |
| MD:3.18mm | ISO 294-4 | 1.3 % | |
| TD：1.59mm | ASTM D955 | 1.1 % | |
| density | ASTM D792 | 0.988 g/cm³ | |
| ISO 1183 | 0.988 g/cm³ | ||
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.3 % |
| TD:3.18mm | ISO 294-4 | 1.2 % | |
| MD:1.59mm | ISO 294-4 | 2.1 % |
| aging | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| Change rate of tensile strength in air | 70°C,168hr | ASTM D573 | -9.0 % |
| 100%Strain,100°C,168hr | ASTM D573 | -2.0 % | |
| volume change | 100°C,168hr,inIRM903Oil | ASTM D471 | 38 % |
| Change rate of tensile strength in air | 100°C,168hr | ASTM D573 | -11 % |
| volume change | 24°C,168hr,inReferenceFuelB | ASTM D471 | 9.0 % |
| Change rate of tensile strength in air | 100%Strain100°C,168hr | ISO 188 | -2.0 % |
| 100%Strain,70°C,168hr | ASTM D573 | -4.0 % | |
| volume change | 24°C,168hr,inReferenceFuelB | ISO 1817 | 9.0 % |
| 100°C,168hr,inIRM903Oil | ISO 1817 | 38 % | |
| Change rate of tensile strength in air | 100%Strain70°C,168hr | ISO 188 | -4.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr | ASTM D573 | 3.0 % |
| volume change | 100°C,168hr,在水中 | ASTM D471 | -7.0 % |
| Change rate of tensile strength in air | 100°C,168hr | ISO 188 | -11 % |
| 70°C,168hr | ISO 188 | -9.0 % | |
| Tensile stress change rate | 70°C,168hr，断裂 | ISO 1817 | 2.0 % |
| volume change | 100°C,168hr,inASTM#1Oil | ASTM D471 | 2.0 % |
| Tensile stress change rate | 100°C,168hr，断裂 | ISO 1817 | 3.0 % |
| volume change | 100°C,168hr,在水中 | ISO 1817 | -7.0 % |
| 100°C,168hr,inASTM#1Oil | ISO 1817 | 2.0 % | |
| Change rate of ultimate elongation in air | 70°C,168hr | ASTM D573 | 2.0 % |
| elastomer | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 370 % |
| compression set | 70°C,22hr | ASTM D395B | 45 % |
| tensile strength | 屈服,23°C | ASTM D412 | 7.83 MPa |
| tear strength | 24°C | ASTM D624 | 26.1 kN/m |
| tensile strength | 100%应变,23°C | ISO 37 | 1.67 MPa |
| compression set | 100°C,22hr | ISO 815 | 72 % |
| Stretch permanent deformation | 100%应变 | ASTM D412 | 15 % |
| compression set | 100°C,22hr | ASTM D395B | 72 % |
| elongation | 断裂,23°C | ISO 37 | 370 % |
| compression set | 70°C,22hr | ISO 815 | 45 % |
| tensile strength | 屈服,23°C | ISO 37 | 7.83 MPa |
| 100%应变 | ASTM D412 | 1.67 MPa | |
| compression set | 24°C,22hr | ISO 815 | 27 % |
| 24°C,22hr | ASTM D395B | 27 % |
| Thermal performance | Test Condition | Test Method | USA Advanced/DuraGrip® DGR 6070NC |
|---|---|---|---|
| brittle temperature | ISO 812 | -65.0 °C | |
| ASTM D746 | -65.0 °C |