| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.17 g/cm³ |
| Shrinkage rate | | 内部方法 | 1.2-1.6 % |
| Shrinkage rate | | ASTM D955 | 0.50-0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 115 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 92.0 % |
| Haze ratio | | 内部方法 | <1.0 % |
| Haze ratio | | ASTM D1003 | <1.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | <1.0 % |
| Shrinkage rate | | 内部方法 | <1.5 % |
| Shrinkage rate | | 内部方法 | <1.0 % |
| MicrowaveBoiling-OvenPower | | 内部方法 | <2200 Watts |
| MicrowaveSteamSterilization-TotalEnergy | | 内部方法 | <11200 W-min |
| ThermalShock-WaterImmersion | | 内部方法 | Noeffect |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1590 Mpa |
| Tensile modulus | | ISO 527-2 | 1620 Mpa |
| tensile strength | | ASTM D638 | 44.0 Mpa |
| tensile strength | | 内部方法 | 44.0 Mpa |
| tensile strength | | 内部方法 | 45.0 Mpa |
| tensile strength | | ISO 527-2 | 45.0 Mpa |
| tensile strength | | ASTM D638 | 53.0 Mpa |
| tensile strength | | ISO 527-2 | 49.0 Mpa |
| elongation | | 内部方法 | 7.0 % |
| elongation | | 内部方法 | 6.5 % |
| elongation | | ASTM D638 | 7.0 % |
| Tensile strain | | ISO 527-2 | 7.0 % |
| elongation | | ASTM D638 | 140 % |
| Tensile strain | | ISO 527-2 | 130 % |
| Flexural modulus | | ASTM D790 | 1590 Mpa |
| Flexural modulus | | ISO 178 | 1530 Mpa |
| bending strength | | ASTM D790 | 66.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 650 J/m |
| Impact strength of cantilever beam gap | | 内部方法 | 640 J/m |
| Impact strength of cantilever beam gap | | 内部方法 | 650 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 14 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 66 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D4812 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D4812 | NoBreak |
| Dart impact | | ASTM D3763 | 63.0 J |
| Dart impact | | ASTM D3763 | 59.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 109 °C |
| Heat distortion temperature | | ASTM D648 | 92.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.