Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCTG 401 EASTMAN USA
Tritan™
Household daily necessiti、Electrical applications
Easy to process、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C2 | 内部方法 | 650 J/m |
| Dart impact | 23°C,EnergyatMaxLoad | ASTM D3763 | 59.0 J |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 130 J/m |
| 23°C3 | 内部方法 | 640 J/m | |
| 23°C | ASTM D256 | 650 J/m | |
| 23°C | ISO 180 | 66 kJ/m² | |
| Dart impact | -40°C,EnergyatMaxLoad | ASTM D3763 | 63.0 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | NoBreak |
| -40°C | ASTM D4812 | NoBreak | |
| -40°C | ISO 180 | 14 kJ/m² |
| hardness | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 115 |
| Supplementary Information | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| MicrowaveBoiling-OvenPower | 内部方法 | <2200 Watts | |
| Shrinkage rate | Boiling,1hr | 内部方法 | <1.0 % |
| Boiling,2hr | 内部方法 | <1.5 % | |
| ThermalShock-WaterImmersion | 35to98°C | 内部方法 | Noeffect |
| MicrowaveSteamSterilization-TotalEnergy | 内部方法 | <11200 W-min | |
| Shrinkage rate | Dishwasher | 内部方法 | <1.0 % |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 1590 Mpa |
| 23°C | ISO 527-2 | 1620 Mpa | |
| tensile strength | 屈服,23°C2 | 内部方法 | 44.0 Mpa |
| 断裂,23°C | ISO 527-2 | 49.0 Mpa | |
| 屈服,23°C | ASTM D638 | 44.0 Mpa | |
| 断裂,23°C | ASTM D638 | 53.0 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 130 % |
| tensile strength | 屈服,23°C3 | 内部方法 | 45.0 Mpa |
| 屈服,23°C | ISO 527-2 | 45.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 7.0 % |
| Flexural modulus | 23°C | ISO 178 | 1530 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 7.0 % |
| bending strength | 屈服,23°C | ASTM D790 | 66.0 Mpa |
| elongation | 屈服,23°C3 | 内部方法 | 6.5 % |
| Flexural modulus | 23°C | ASTM D790 | 1590 Mpa |
| elongation | 屈服,23°C2 | 内部方法 | 7.0 % |
| 断裂,23°C | ASTM D638 | 140 % |
| optical performance | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| transmissivity | 总计 | ASTM D1003 | 92.0 % |
| Haze ratio | --2 | 内部方法 | <1.0 % |
| -- | ASTM D1003 | <1.0 % |
| physical property | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| Shrinkage rate | MD：BlowMolded | 内部方法 | 1.2-1.6 % |
| density | ASTM D792 | 1.17 g/cm³ | |
| Shrinkage rate | MD：注塑 | ASTM D955 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/401 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 92.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 109 °C |