PA6 GFR 60 NATURAL
0
- Properties:Glass fiber reinforced material60%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ash content | ISO 3451 | 59 to 61 % | |
| density | ISO 1183 | 1.12 to 1.14 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.25 % | |
| 0.15 | |||
| Water absorption rate | ISO 62 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 280 to 320 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 21 to 25 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 21 to 25 kJ/m² | |
| Hardness (Shore) | ISO 868 | 91 to 94 | |
| Tensile modulus | ISO 527-2 | 17000 to 18000 MPa | |
| tensile strength | ISO 527-2 | 240 to 260 MPa | |
| Tensile strain | ISO 527-2 | 2.0 to 2.5 % | |
| Flexural modulus | ISO 178 | 14000 to 16000 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 215 | |
| vicat | ISO 306/B | 215 ℃ | |
| melting temperature | ISO 3146 | 215 to 225 ℃ | |
| UL flame retardant rating | UL 94 | HB | |
| Hot deformation temperature (HDT) | ISO 75-2/B | 225 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.