PA6 GFR 60 NATURAL 土耳其EPSAN
--
--
玻璃纤维增强材料,60%,填料按重量
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 土耳其EPSAN/GFR 60 NATURAL |
|---|---|---|---|
| Hardness (Shore) | 支撐 D | ISO 868 | 91 to 94 |
| bending strength | 23℃ | ISO 178 | 280 to 320 MPa |
| tensile strength | 断裂, 23℃ | ISO 527-2 | 240 to 260 MPa |
| Flexural modulus | 23℃ | ISO 178 | 14000 to 16000 MPa |
| Tensile modulus | 23℃ | ISO 527-2 | 17000 to 18000 MPa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 21 to 25 kJ/m² |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 2.0 to 2.5 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 21 to 25 kJ/m² |
| physical property | Test Condition | Test Method | 土耳其EPSAN/GFR 60 NATURAL |
|---|---|---|---|
| Shrinkage rate | TD: 3.00 mm | ISO 294-4 | 0.25 % |
| ash content | ISO 3451 | 59 to 61 % | |
| Water absorption rate | 饱和, 23℃ | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.12 to 1.14 g/cm³ | |
| Shrinkage rate | MD: 3.00 mm | 0.15 |
| Thermal performance | Test Condition | Test Method | 土耳其EPSAN/GFR 60 NATURAL |
|---|---|---|---|
| melting temperature | ISO 3146 | 215 to 225 ℃ | |
| vicat | ISO 306/B | 215 ℃ | |
| Hot deformation temperature (HDT) | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 215 |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| Hot deformation temperature (HDT) | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 225 ℃ |