Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.19 % |
| density | | ASTM D792 | 1.10 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Barcol Hardness | | ASTM D2583 | 52 |
| Rockwell hardness | | ASTM D785 | 97 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HotFormingTemperature | | 内部方法 | 177to193 °C |
| HotFormingTemperature | | 内部方法 | 149to171 °C |
| CyclesFreeze-Thaw | | 内部方法 | NoEffect |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2620 MPa |
| Flexural modulus | | ASTM D790 | 2140 MPa |
| elongation | | ASTM D638 | 5.0 % |
| tensile strength | | ASTM D638 | 44.8 MPa |
| bending strength | | ASTM D790 | 74.5 MPa |
| bending strength | | ASTM D790 | 68.9 MPa |
| Flexural modulus | | ASTM D790 | 2160 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | 内部方法 | >40.7 J |
| Impact strength of cantilever beam gap | | ASTM D256A | 130 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 7.9E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 89.4 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.