Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.27 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 9.0 g/10min |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| Water absorption rate | | ASTMD570 | 0.25 % |
| Water absorption rate | | ASTMD570 | 1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 109 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | 5VA |
| Limiting Oxygen Index | | ASTMD2863 | 47 % |
| NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 0.700 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural Strength4 | | ASTMD790 | 165 Mpa |
| Poisson's ratio | | ASTMD638 | 0.36 |
| | ASTMD1044 | 10.0 mg |
| Tensile modulus | | ASTMD638 | 3590 Mpa |
| tensile strength | | ASTMD638 | 110 Mpa |
| elongation | | ASTMD638 | 7.0 % |
| elongation | | ASTMD638 | 60 % |
| Flexural modulus | | ASTMD790 | 3520 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 53 J/m |
| Impact strength of cantilever beam gap | | ASTMD4812 | 1300 J/m |
| ReverseNotchIzodImpact | | ASTMD256 | 1300 J/m |
| Falling hammer impact | | ASTMD3029 | 36.6 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Hot wire ignition (HWI) | | UL746 | PLC 1 |
| Volume resistivity | | ASTMD257 | 1E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 33 KV/mm |
| dielectric strength | | ASTMD149 | 28 KV/mm |
| dielectric strength | | ASTMD149 | 20 KV/mm |
| dielectric constant | | ASTMD150 | 3.15 |
| dielectric constant | | ASTMD150 | 3.15 |
| Dissipation Factor | | ASTMD150 | 1.5E-03 |
| Dissipation Factor | | ASTMD150 | 1.2E-03 |
| Dissipation Factor | | ASTMD150 | 2.5E-03 |
| Arc resistance 6 | | ASTMD495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 4 |
| High arc combustion index (HAI) | | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 210 °C |
| | ASTMD648 | 201 °C |
| vicat | | ASTMD15255 | 219 °C |
| | ASTME831 | 5.6E-05 cm/cm/°C |
| | ASTME831 | 5.4E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.22 W/m/K |
| RTI Elec | | UL746 | 170 °C |
| RTI Imp | | UL746 | 170 °C |
| RTI Str | | UL746 | 170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.