PC 1000 SABIC INNOVATIVE SAUDI
SABIC®
Electrical applications、Lighting applications、Automotive Applications
Thermal stability、Middle flow
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 53 J/m |
| Falling hammer impact | 23°C | ASTMD3029 | 36.6 J |
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 1300 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | 1300 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTMD785 | 109 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| elongation | 屈服 | ASTMD638 | 7.0 % |
| 断裂 | ASTMD638 | 60 % | |
| Flexural modulus | 100mmSpan | ASTMD790 | 3520 Mpa |
| tensile strength | 屈服 | ASTMD638 | 110 Mpa |
| Flexural Strength4 | Yield,100mmSpan | ASTMD790 | 165 Mpa |
| Tensile modulus | ASTMD638 | 3590 Mpa | |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg | |
| Poisson's ratio | ASTMD638 | 0.36 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 3 |
| Volume resistivity | ASTMD257 | 1E+17 ohms·cm | |
| dielectric constant | 100Hz | ASTMD150 | 3.15 |
| Dissipation Factor | 100Hz | ASTMD150 | 1.5E-03 |
| dielectric constant | 1kHz | ASTMD150 | 3.15 |
| dielectric strength | 1.60mm,在油中 | ASTMD149 | 28 KV/mm |
| 3.20mm,在油中 | ASTMD149 | 20 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 2 |
| Dissipation Factor | 1kHz | ASTMD150 | 1.2E-03 |
| Arc resistance 6 | ASTMD495 | PLC 5 | |
| Dissipation Factor | 2.45GHz | ASTMD150 | 2.5E-03 |
| dielectric strength | 1.60mm,inAir | ASTMD149 | 33 KV/mm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 |
| Limiting Oxygen Index | ASTMD2863 | 47 % | |
| UL flame retardant rating | 3.0mm | UL94 | 5VA |
| 0.40mm | UL94 | V-2 | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 1.3 % |
| density | ASTMD792 | 1.27 g/cm³ | |
| melt mass-flow rate | 337°C/6.6kg | ASTMD1238 | 9.0 g/10min |
| Water absorption rate | 24hr | ASTMD570 | 0.25 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SAUDI/1000 |
|---|---|---|---|
| MD：-20to150°C | ASTME831 | 5.6E-05 cm/cm/°C | |
| TD：-20to150°C | ASTME831 | 5.4E-05 cm/cm/°C | |
| vicat | ASTMD15255 | 219 °C | |
| thermal conductivity | ASTMC177 | 0.22 W/m/K | |
| RTI Str | UL746 | 170 °C | |
| RTI Elec | UL746 | 170 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 201 °C | |
| RTI Imp | UL746 | 170 °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 210 °C |