MS TX POLYMER TX-400S
356
- Properties:transparent
- Usages:CastersElectrical fieldElectronic fieldElectrical appliances
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Total Light Transmittance | ASTM D-100 | 92 % | |
| Haze ratio | ASTM D-100 | 0.2 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | JIS K-6874 | 0.8 g/10min | |
| JIS K-6874 | 11 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D-785 | 87 M | |
| Flexural modulus | ASTM D-790 | 3.430 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 21 J/m | |
| tensile strength | ASTM D-638 | 71 Mpa | |
| bending strength | ASTM D-790 | 119 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 71 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 3.430 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 119 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 87 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.12 | ||
| melt mass-flow rate | ASTM D1238/ISO 1133 | 0.8 g/10min | |
| ASTM D1238/ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D-648 | 87 °C | |
| vicat | JIS K-7206 | 102 °C | |
| combustibility | UL 94 | HB | |
| Combustibility (rate) | UL 94 | HB | |
| vicat | ASTM D1525/ISO R306 | 102 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.