Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MS TX-400S DENKA JAPAN
TX POLYMER
Casters、Electrical field、Electronic field、Electrical appliances
transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/TX-400S |
|---|---|---|---|
| melt mass-flow rate | 200℃，5kgf荷重 | JIS K-6874 | 0.8 g/10min |
| 220℃，5kgf荷重 | JIS K-6874 | 11 g/10min |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/TX-400S |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 119 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | 2mm/min | ASTM D-790 | 3.430 Mpa |
| ASTM D790/ISO 178 | 3.430 kg/cm²(MPa)[Lb/in²] | ||
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 21 J/m |
| tensile strength | 5mm/min | ASTM D-638 | 71 Mpa |
| Rockwell hardness | ASTM D785 | 87 | |
| tensile strength | ASTM D638/ISO 527 | 71 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | 23℃ | ASTM D-785 | 87 M |
| bending strength | 2mm/min | ASTM D-790 | 119 Mpa |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/TX-400S |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 11 g/10min | |
| density | 1.12 |
| physical property | Test Condition | Test Method | DENKA JAPAN/TX-400S |
|---|---|---|---|
| Haze ratio | 2mm | ASTM D-100 | 0.2 % |
| Total Light Transmittance | 2mm | ASTM D-100 | 92 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/TX-400S |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| vicat | 5kgf荷重 | JIS K-7206 | 102 °C |
| ASTM D1525/ISO R306 | 102 ℃（℉） | ||
| combustibility | UL 94 | HB | |
| Heat distortion temperature | 平面方向法18.6kgf应力，HDT | ASTM D-648 | 87 °C |