HIPS

HIPS SEHI-121 IDEMITSU MALASIA

Properties:
Characteristics high impact resistance high fluidity flame retardant form particles
Usages:
Shell
Compare

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.50 mm	UL 94	V-2

squeeze out	Test Condition	Test Method	Test Result
Material barrel temperature			200 to 240 °C
	Material barrel temperature			180 to 220 °C
	Material barrel temperature	Material barrel temperature			160 to 200 °C
drying time			1.0 to 2.0 hr
drying temperature			70.0 °C
Oral mold temperature			190 to 220 °C
Material barrel temperature			200 to 240 °C

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	35 %
tensile strength	Break	ASTM D638	25.1 MPa

injection	Test Condition	Test Method	Test Result
Mold temperature			40.0 to 60.0 °C
Spray nozzle temperature			200 to 230 °C
Temperature at the front of the material cylinder			210 to 240 °C
drying temperature			70.0 °C
Temperature in the middle of the barrel			190 to 220 °C
Temperature at the rear of the barrel			180 to 210 °C
drying time			1.0 to 2.0 hr

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	81.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	200°C/5.0 kg	ASTM D1238	8.0 g/10 min
density		ASTM D792	1.06 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.