Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HIPS SEHI-121 IDEMITSU MALASIA
--
Shell
Characteristics, high impact resistance, high fluidity, flame retardant form, particles
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 35 % |
| tensile strength | 断裂 | ASTM D638 | 25.1 MPa |
| flammability | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| UL flame retardant rating | 1.50 mm | UL 94 | V-2 |
| squeeze out | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| drying temperature | 70.0 °C | ||
| die temperature | 190 to 220 °C | ||
| drying time | 1.0 to 2.0 hr | ||
| Barrel Temperature | 200 to 240 °C |
| physical property | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| density | ASTM D792 | 1.06 g/cm³ | |
| melt mass-flow rate | 200°C/5.0 kg | ASTM D1238 | 8.0 g/10 min |
| injection | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| drying time | 1.0 to 2.0 hr | ||
| Temperature in the middle of the barrel | 190 to 220 °C | ||
| Temperature at the rear of the barrel | 180 to 210 °C | ||
| drying temperature | 70.0 °C | ||
| Temperature at the front of the material cylinder | 210 to 240 °C | ||
| Temperature | 40.0 to 60.0 °C | ||
| Spray nozzle temperature | 200 to 230 °C |
| Thermal performance | Test Condition | Test Method | IDEMITSU MALASIA/SEHI-121 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 81.0 °C |