Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.42 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.25 % |
| Water absorption rate | Saturation | ASTM D570 | 0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 94 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| limiting pv value | | | 1460 psi·fpm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3100 MPa |
| tensile strength | Yield | ASTM D638 | 75.8 MPa |
| elongation | Break | ASTM D638 | 25 % |
| Flexural modulus | | ASTM D790 | 2900 MPa |
| bending strength | | ASTM D790 | 110 MPa |
| compressive strength | | ASTM D695 | 35.9 MPa |
| coefficient of friction | Itself - Dynamic | | 0.20 |
| Wear factor | | ASTM D3702 | 110 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 80 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| dielectric constant | | ASTM D150 | 3.70 |
| Dissipation Factor | | ASTM D150 | 5E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 169 °C |
| Heat distortion temperature | | ASTM D648 | 125 °C |
| melting temperature | | ASTM D2133 | 175 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.2E-04 cm/cm/°C |
| maximum service temperature | | UL 746B | 85 °C |
| maximum service temperature | | | 149 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare