Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.11 g/cm³ |
| Melt volume flow rate | | ISO1133 | 13.0 cm³/10min |
| Melt volume flow rate | | ISO1133 | 34.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 725 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 725 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 725 °C |
| UL flame retardant rating | | UL94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ASTMD638 | 15 % |
| fracture | | ISO527-2/50 | 18 % |
| yield | | ASTMD790 | 2100 MPa |
| yield | | ASTMD638 | 43.0 MPa |
| yield | | ISO527-2/50 | 42.0 MPa |
| fracture | | ASTMD638 | 43.0 MPa |
| fracture | | ISO527-2/50 | 42.0 MPa |
| yield | | ASTMD638 | 1.0 % |
| yield | | ISO527-2/50 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257,IEC60093 | 1E+16 ohms |
| Volume resistivity | | ASTMD257,IEC60093 | 3E+16 ohms·cm |
| Dissipation Factor | | ASTMD150,IEC60250 | 3.5E-03 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| CTI | | IEC60112 | 250 V |
| Hot wire ignition (HWI) | | UL746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI | | UL746 | 65.0 °C |
| Linear thermal expansion coefficient | | ASTME831,ISO11359-2 | 9.4E-05 cm/cm/°C |
| Linear thermal expansion coefficient | | ASTME831,ISO11359-2 | 9.6E-05 cm/cm/°C |
| RTI Elec | | UL746 | 65.0 °C |
| RTI Imp | | UL746 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.