PPO(PPE)+PS NORYL™ RN0612 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
-30°C | ISO 179/1eA | 3.0 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
fracture | ISO 527-2/50 | 42.0 MPa | |
ISO 527-2/50 | 18 % | ||
ASTM D638 | 15 % | ||
yield | ASTM D638 | 1.0 % | |
ASTM D638 | 43.0 MPa | ||
ISO 527-2/50 | 2.0 % | ||
fracture | ASTM D638 | 43.0 MPa | |
yield | ISO 527-2/50 | 42.0 MPa | |
ASTM D790 | 2100 MPa |
Electrical performance | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
Volume resistivity | ASTMD257 | 3E+16 ohms·cm | |
Dissipation Factor | 1MHz | ASTMD150 | 3.5E-03 |
Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
Surface Resistivity | ASTMD257 | 1E+16 ohms |
flammability | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
UL flame retardant rating | 3.00mm | UL 94 | V-0 |
Hot filament ignition temperature | 2.00mm | IEC 60695-2-13 | 725 °C |
3.00mm | IEC 60695-2-13 | 725 °C | |
1.00mm | IEC 60695-2-13 | 725 °C | |
UL flame retardant rating | 1.50mm | UL 94 | V-1 |
Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
physical property | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 34.0 cm³/10min |
density | ASTMD792 | 1.11 g/cm³ | |
Melt volume flow rate | 280°C/1.2kg | ISO 1133 | 13.0 cm³/10min |
Thermal performance | Test Condition | Test Method | SABIC/NORYL™ RN0612 resin |
---|---|---|---|
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 9.6E-05 cm/cm/°C |
RTI Imp | UL 746 | 65.0 °C | |
RTI | UL 746 | 65.0 °C | |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 9.4E-05 cm/cm/°C |
RTI Elec | UL 746 | 65.0 °C |