Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.27 g/cm³ |
| Water absorption rate | Saturation | ASTM D570 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 105 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.567 |
| transmissivity | | ASTM D1003 | 90.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2010 MPa |
| tensile strength | Break | ASTM D638 | 27.6 MPa |
| elongation | Yield | ASTM D638 | 180 % |
| bending strength | Yield | ASTM D790 | 68.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 91 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 37 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 2E+14 ohms |
| Volume resistivity | | ASTM D257 | 6E+15 ohms·cm |
| Dissipation Factor | | ASTM D150 | 0.020 |
| arc resistance | | ASTM D495 | 125 sec |
| dielectric strength | | ASTM D149 | 15 kV/mm |
| dielectric constant | | ASTM D150 | 3.40 |
| dielectric constant | | ASTM D150 | 3.20 |
| Dissipation Factor | | ASTM D150 | 0.010 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTMC177 | 0.21 W/m/K |
| Heat distortion temperature | | ASTM D648 | 70.0 °C |
| Heat distortion temperature | | ASTM D648 | 62.8 °C |
| Continuous use temperature | | ASTM D794 | 65.0 °C |
| Glass Transition Temperature | | ASTME1356 | 81.1 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9.2E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1460 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.