Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.53 g/cm³ |
| SpiralFlow | | 内部方法 | 10.0 cm |
| SpiralFlow | | 内部方法 | 44.0 cm |
| Shrinkage rate | | ISO294-4 | 0.90 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| Water absorption rate - saturation | | ISO62 | 0.60 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| LossTangent | | IEC60250 | 0.00400 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 12000 MPa |
| Tensile stress | | ISO527-2 | 195 MPa |
| Tensile stress | | ISO527-2 | 130 MPa |
| Tensile stress | | ISO527-2 | 80.0 MPa |
| Tensile stress | | ISO527-2 | 50.0 MPa |
| Tensile strain | | ISO527-2 | 2.8 % |
| Flexural modulus | | ISO178 | 11000 MPa |
| Bending stress | | ISO178 | 280 MPa |
| Bending stress | | ISO178 | 180 MPa |
| Bending stress | | ISO178 | 120 MPa |
| Bending stress | | ISO178 | 70.0 MPa |
| compression stress | | ISO604 | 290 MPa |
| compression stress | | ISO604 | 190 MPa |
| compression stress | | ISO604 | 75.0 MPa |
| compression stress | | ISO604 | 50.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1U | 70 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 11 kJ/m² |
| | ISO180 | 60 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO11443 | 600 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 22 kV/mm |
| dielectric constant | | IEC60250 | 3.30 |
| CTI | | IEC60112 | 150 V |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/Af | 380 °C |
| Glass Transition Temperature | | ISO11357-2 | 162 °C |
| Glass Transition Temperature | | ISO11357-2 | 169 °C |
| melting temperature | | ISO11357-3 | 387 °C |
| | ISO11359-2 | 2.1E-05 cm/cm/°C |
| | ISO11359-2 | 2.3E-05 cm/cm/°C |
| | ISO11359-2 | 4E-05 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| thermal conductivity | | ISO22007-4 | 0.30 W/m/K |
| thermal conductivity | | ISO22007-4 | 0.35 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.