PEEK LNP™ THERMOCOMP™ LF-1002
147
- Properties:Hydrolysis resistanceThermal stability
- Usages:Automotive componentsHome appliance componentsElectronic and electrical components
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.30to0.60 % | |
| ASTMD955 | 0.50to0.80 % | ||
| Water absorption rate | ASTMD570 | 0.070 % | |
| ISO62 | 0.12 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTMD638 | 6080 Mpa | |
| ISO527-2/1 | 6500 Mpa | ||
| tensile strength | ASTMD638 | 120 Mpa | |
| Tensile stress | ISO527-2/5 | 125 Mpa | |
| tensile strength | ASTMD638 | 114 Mpa | |
| Tensile stress | ISO527-2/5 | 122 Mpa | |
| elongation | ASTMD638 | 3.4 % | |
| Tensile strain | ISO527-2/5 | 3.4 % | |
| elongation | ASTMD638 | 4.2 % | |
| Tensile strain | ISO527-2/5 | 4.0 % | |
| Flexural modulus | ASTMD790 | 6010 Mpa | |
| ISO178 | 5670 Mpa | ||
| bending strength | ASTMD790 | 203 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam notch impact strength 6 | ISO180/1A | 4.6 kJ/m² | |
| Unscented Izod Impact Strength 5 | ISO180/1U | 50 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 8.80 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.50 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD696 | 4.4E-05 cm/cm/°C | ||
| ASTMD648 | 326 °C | ||
| Hot deformation temperature 7 | ISO75-2/Bf | 285 °C | |
| ASTMD648 | 169 °C | ||
| Hot deformation temperature 7 | ISO75-2/Af | 171 °C | |
| ASTMD696 | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.