Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.60到0.80 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.50到0.90 % |
| PostShrinkage | | ISO2577 | 0.70到1.0 % |
| density | | ISO1183 | 1.80到1.90 g/cm³ |
| Water absorption rate | | ISO62 | <1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >20.0 MPa |
| CompressionMoldingTemperature | | | 160到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604 | 200到250 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 7000到9000 MPa |
| Tensile modulus | Injection | ISO527-2 | 8000到10000 MPa |
| Tensile stress | | ISO527-2 | 40.0到50.0 MPa |
| Tensile stress | Injection | ISO527-2 | 45.0到60.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 9000到11000 MPa |
| Flexural modulus | Injection | ISO178 | 10000到12000 MPa |
| Bending stress | Compression Molded | ISO178 | 90.0到110 MPa |
| Bending stress | Injection | ISO178 | 100到120 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.5到3.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 2.5到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 4.0到7.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 7.0到9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC60093 | 1.0E+11到1.0E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 20到30 kV/mm |
| | IEC60250 | 11.016.0 |
| | IEC60250 | 7.009.00 |
| Dissipation Factor | | IEC60250 | 0.20到0.40 |
| Dissipation Factor | | IEC60250 | 0.020到0.040 |
| arc resistance | | ASTMD495 | PLC 5 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | IEC60216 | 150 °C |
| | ISO75-2/A | >200 °C |
| | ISO75-2/C | 130到150 °C |
| | ISO11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.50到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare