Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MF MELOPAS® MF 156 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 注塑 | ISO 179/1eU | 7.0to9.0 kJ/m² |
| 模压成型 | ISO 179/1eU | 4.0to7.0 kJ/m² | |
| Charpy Notched Impact Strength | 模压成型 | ISO 179/1eA | 1.5to3.0 kJ/m² |
| 注塑 | ISO 179/1eA | 2.5to4.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| Compression molding pressure | >20.0 MPa | ||
| Compression molding temperature | 160to180 °C |
| Electrical performance | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 20to30 kV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+11到1.0E+12 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 11.016.0 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.20to0.40 |
| arc resistance | ASTM D495 | PLC 5 | |
| relative permittivity | 1MHz | IEC 60250 | 7.009.00 |
| Surface Resistivity | IEC 60093 | 1.0E+10到1.0E+11 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020to0.040 |
| Mechanical properties | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| tensile strength | CompressionMolded | ISO 527-2 | 40.0to50.0 MPa |
| bending strength | 注塑 | ISO 178 | 100to120 MPa |
| Flexural modulus | 注塑 | ISO 178 | 10000to12000 MPa |
| compression stress | ISO 604 | 200to250 MPa | |
| Tensile modulus | 模压成型 | ISO 527-2 | 7000to9000 MPa |
| Flexural modulus | 模压成型 | ISO 178 | 9000to11000 MPa |
| tensile strength | 注塑 | ISO 527-2 | 45.0to60.0 MPa |
| bending strength | 模压成型 | ISO 178 | 90.0to110 MPa |
| Tensile modulus | 注塑 | ISO 527-2 | 8000to10000 MPa |
| flammability | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 900 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.70to1.0 % | |
| Apparent density | ISO 60 | 0.60to0.80 g/cm³ | |
| Water absorption rate | 23°C,24hr | ISO 62 | <1.0 % |
| Shrinkage rate | MD2 | ISO 2577 | 0.50to0.90 % |
| density | ISO 1183 | 1.80to1.90 g/cm³ |
| Thermal performance | Test Condition | Test Method | RASCHIG GmbH/MELOPAS® MF 156 |
|---|---|---|---|
| maximum service temperature | 20,000h | IEC 60216 | 150 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 130to150 °C |
| thermal conductivity | ASTME1461 | 0.50to0.60 W/m/K | |
| maximum service temperature | <50h | IEC 60216 | 200 °C |