Technical Data Sheet
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | BS903 | 2.32 MPa |
| elongation | Break | BS903 | 280 % |
| PeelStrength | | | 14.2 N/mm |
| Tensile modulus | | | 0.650 MPa |
| Tensile modulus | | BS903 | 0.910 MPa |
| compression set | | | 45 % |
| tear strength | | BS903 | 5.50 kN/m |
| LinearShrinkage | | | <1.0 % |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | BS903 | 1.05 g/cm³ |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 7.0 hr |
| TackFreeTime | | | 4.0 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| IRHD hardness | | BS903 | 39 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| VolumetricExpansion | | | 8.8E-04 cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 7.8E+15 ohms |
| Volume resistivity | | ASTMD257 | 4.7E+14 ohms·cm |
| dielectric constant | | ASTMD150 | 3.20 |
| Dissipation Factor | | ASTMD150 | 1.2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 2.9E-04 cm/cm/°C |
| thermal conductivity | | | 0.20 W/m/K |
| Service | | | -60到250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.