PP Homopolymer WPP PP PPH2GF3-Black Washington Penn Plastic Co. Inc.

0
  • Properties:
    Filler
    glass fiber reinforced material
    30%
    filler by weight
  • Usages:
    Applications in the automotive industry and consumer goods applications

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
melt mass-flow rateISO 11334.5 g/10min
densityASTM D7921.12 g/cm³
densityISO 11831.12 g/cm³
melt mass-flow rateASTM D12384.5 g/10min
hardnessTest ConditionTest MethodTest Result
Shore hardnessASTM D224075
Mechanical propertiesTest ConditionTest MethodTest Result
UltimateTensileStrengthISO 52780.0 MPa
tensile strength YieldISO 527-2/5075.0 MPa
tensile strength BreakASTM D63878.0 MPa
tensile strength BreakISO 527-278.0 MPa
tensile strength BreakISO 527-2/5088.0 MPa
Tensile strainYieldISO 527-2/506.5 %
Tensile strainBreakISO 527-2/506.5 %
Flexural modulusASTM D7905100 MPa
Flexural modulusISO 1785400 MPa
bending strengthISO 178118 MPa
elongationBreakASTM D6386.0 %
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact StrengthISO 1799.5 kJ/m²
Impact strength of simply supported beam without notchISO 17943 kJ/m²
Impact strength of cantilever beam gapASTM D25695 J/m
Impact strength of cantilever beam gapISO 1806.5 kJ/m²
Impact strength of cantilever beam gapISO 1809.0 kJ/m²
Suspended wall beam without notch impact strengthISO 18035 kJ/m²
Impact strength of cantilever beam gapASTM D256600 J/m
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/Af141 °C
vicatASTM D1525161 °C
Heat distortion temperatureISO 75-2/B156 °C
Heat distortion temperatureASTM D648148 °C
Heat distortion temperatureISO 75-2/A146 °C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.