PP Homopolymer WPP PP PPH2GF3-Black Washington Penn Plastic Co. Inc.
--
Applications in the automotive industry and consumer goods applications
Filler, glass fiber reinforced material, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPH2GF3-Black |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 9.5 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 600 J/m |
Suspended wall beam without notch impact strength | 23°C | ISO 180 | 35 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 9.0 kJ/m² |
-40°C | ISO 180 | 6.5 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 43 kJ/m² |
hardness | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPH2GF3-Black |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 75 |
Mechanical properties | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPH2GF3-Black |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 6.0 % |
tensile strength | 断裂 | ASTM D638 | 78.0 MPa |
断裂 | ISO 527-2 | 78.0 MPa | |
Flexural modulus | ASTM D790 | 5100 MPa | |
ISO 178 | 5400 MPa | ||
Tensile strain | 断裂 | ISO 527-2/50 | 6.5 % |
屈服 | ISO 527-2/50 | 6.5 % | |
tensile strength | 屈服 | ISO 527-2/50 | 75.0 MPa |
bending strength | ISO 178 | 118 MPa | |
UltimateTensileStrength | ISO 527 | 80.0 MPa | |
tensile strength | 断裂 | ISO 527-2/50 | 88.0 MPa |
physical property | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPH2GF3-Black |
---|---|---|---|
melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 4.5 g/10min |
density | ASTM D792 | 1.12 g/cm³ | |
ISO 1183 | 1.12 g/cm³ | ||
melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 4.5 g/10min |
Thermal performance | Test Condition | Test Method | Washington Penn Plastic Co. Inc./WPP PP PPH2GF3-Black |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 141 °C |
vicat | ASTM D1525 | 161 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 148 °C |
0.45MPa,未退火,HDT | ISO 75-2/B | 156 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 146 °C |