Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 15 g/10min |
| Melt volume flow rate | | ISO1133 | 15.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.40到0.80 % |
| Shrinkage rate | | 内部方法 | 0.40到0.80 % |
| Shrinkage rate | | 内部方法 | 0.60到1.0 % |
| Shrinkage rate | | 内部方法 | 0.60到1.0 % |
| Water absorption rate | | ISO62 | 0.16 % |
| Water absorption rate | | ISO62 | 0.050 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 119 |
| | ISO2039-1 | 110 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| --3 | | ASTMD638 | 9950 Mpa |
| Surrender 4 | | ASTMD638 | 115 Mpa |
| yield | | ISO527-2/5 | 145 Mpa |
| Fracture 5 | | ASTMD638 | 115 Mpa |
| fracture | | ISO527-2/5 | 145 Mpa |
| Surrender 6 | | ASTMD638 | 2.0 % |
| yield | | ISO527-2/5 | 2.4 % |
| Fracture 7 | | ASTMD638 | 2.0 % |
| fracture | | ISO527-2/5 | 2.5 % |
| 50.0mm span 8 | | ASTMD790 | 8450 Mpa |
| --9 | | ISO178 | 8500 Mpa |
| --10 | | ISO178 | 210 Mpa |
| Yield, 50.0mm span 11 | | ASTMD790 | 165 Mpa |
| | 内部方法 | 30.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| The impact strength of a simply supported beam without a notch is 13 | | ISO179/1eU | 45 kJ/m² |
| Impact strength of simply supported beam gap 12 | | ISO179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam gap 12 | | ISO179/1eA | 9.0 kJ/m² |
| The impact strength of a simply supported beam without a notch is 13 | | ISO179/1eU | 40 kJ/m² |
| -30°C | | ASTMD256 | 48 J/m |
| 23°C | | ASTMD256 | 57 J/m |
| -30°C14 | | ISO180/1A | 8.0 kJ/m² |
| 0°C15 | | ISO180/1A | 8.0 kJ/m² |
| 23°C16 | | ISO180/1A | 9.0 kJ/m² |
| -30°C | | ASTMD4812 | 470 J/m |
| 23°C | | ASTMD4812 | 480 J/m |
| -30°C17 | | ISO180/1U | 40 kJ/m² |
| 23°C18 | | ISO180/1U | 45 kJ/m² |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 8.00 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 3.60 |
| | IEC60250 | 3.20 |
| Dissipation Factor | | IEC60250 | 8E-04 |
| Dissipation Factor | | IEC60250 | 8E-04 |
| Dissipation Factor | | IEC60250 | 0.013 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| CTI | | IEC60112 | 300 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 27 KV/mm |
| dielectric strength | | IEC60243-1 | 23 KV/mm |
| dielectric strength | | IEC60243-1 | 15 KV/mm |
| | IEC60250 | 3.30 |
| | IEC60250 | 3.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Flow: 23 to 60 ° C | | ISO11359-2 | 2.2E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | | ASTME831 | 7.5E-05 cm/cm/°C |
| Horizontal: 23 to 60 ° C | | ISO11359-2 | 8.1E-05 cm/cm/°C |
| 0.45MPa, Unanealed, 3.20mm | | ASTMD648 | 208 °C |
| 0.45MPa, Unanealed, 100mm span 19 | | ISO75-2/Be | 217 °C |
| 1.8MPa, Unanealed, 3.20mm | | ASTMD648 | 190 °C |
| 1.8MPa, Unanealed, 100mm span 20 | | ISO75-2/Ae | 195 °C |
| BallPressure Test | | IEC60695-10-2 | Pass |
| Flow: -40 to 40 ° C | | ASTME831 | 2.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.