PBT/PET 8032UX SABIC INNOVATIVE US
VALOX™
chip、Shell、Home appliance components、Phone case
enhance、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
23°C | ISO 180/1A | 9.0 kJ/m² | |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
-30°C | ASTM D256 | 48 J/m | |
ASTM D4812 | 470 J/m | ||
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
23°C | ISO 180/1U | 45 kJ/m² | |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
23°C | ASTM D256 | 57 J/m | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
-30°C | ISO 180/1A | 8.0 kJ/m² | |
23°C | ASTM D4812 | 480 J/m | |
0°C | ISO 180/1A | 8.0 kJ/m² | |
-30°C | ISO 180/1U | 40 kJ/m² |
hardness | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
Rockwell hardness | R计秤 | ISO 2039-2 | 119 |
ball-indentation hardness | H358/30 | ISO 2039-1 | 110 Mpa |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
yield | ASTM D638 | 115 Mpa | |
fracture | ISO 527-2/5 | 145 Mpa | |
yield | ASTM D638 | 2.0 % | |
Yield, 50.0mm span | ASTM D790 | 165 Mpa | |
--3 | ASTM D638 | 9950 Mpa | |
yield | ISO 527-2/5 | 145 Mpa | |
ISO 527-2/5 | 2.4 % | ||
fracture | ASTM D638 | 115 Mpa | |
--10 | ISO 178 | 210 Mpa | |
fracture | ASTM D638 | 2.0 % | |
--9 | ISO 178 | 8500 Mpa | |
Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 30.0 mg |
50.0mm span | ASTM D790 | 8450 Mpa | |
fracture | ISO 527-2/5 | 2.5 % |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
relative permittivity | 60Hz | IEC 60250 | 3.30 |
dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 27 KV/mm |
relative permittivity | 50Hz | IEC 60250 | 3.30 |
100Hz | IEC 60250 | 3.60 | |
dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 15 KV/mm |
relative permittivity | 1MHz | IEC 60250 | 3.20 |
Dissipation Factor | 50Hz | IEC 60250 | 8E-04 |
60Hz | IEC 60250 | 8E-04 | |
1MHz | IEC 60250 | 0.013 | |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 23 KV/mm |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
flammability | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
UL flame retardant rating | 1.60mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
Shrinkage rate | TD2 | 内部方法 | 0.60-1.0 % |
MD:3.20mm | 内部方法 | 0.40-0.80 % | |
melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 15 g/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
饱和,23°C | ISO 62 | 0.16 % | |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.60-1.0 % |
Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 15.0 cm3/10min |
Shrinkage rate | MD1 | 内部方法 | 0.40-0.80 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/8032UX |
---|---|---|---|
Flow: 23 to 60 ° C | 23到60℃ | ISO 11359-2 | 2.2E-05 cm/cm/°C |
0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 217 °C | |
Flow: -40 to 40 ° C | ASTME831 | 2.5E-05 cm/cm/°C | |
Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 7.5E-05 cm/cm/°C |
1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 195 °C | |
1.8MPa, Unanealed, 3.20mm | ASTM D648 | 190 °C | |
Horizontal: 23 to 60 ° C | 横向, 23到60℃ | ISO 11359-2 | 8.1E-05 cm/cm/°C |
0.45MPa, Unanealed, 3.20mm | ASTM D648 | 208 °C | |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |