HDPE MAJORIS AG100E
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.00 g/cm³ | |
| melt mass-flow rate | ISO1133 | 0.20 g/10min | |
| ISO1133 | 18 g/10min | ||
| ISO1133 | 0.60 g/10min | ||
| Shrinkage rate | 0.90 % | ||
| 1.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO178 | 1490 MPa | |
| Bending stress | ISO178 | 47.0 MPa | |
| Tensile modulus | ISO527-2/1 | 1800 MPa | |
| Tensile stress | Yield | ISO527-2/50 | 30.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 17 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 70 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/B | 106 °C | ||
| ISO75-2/A | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.