HDPE MAJORIS AG100E AD MAJORIS FRANCE
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AD MAJORIS FRANCE/MAJORIS AG100E |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | AD MAJORIS FRANCE/MAJORIS AG100E |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1490 MPa | |
| Tensile modulus | ISO 527-2/1 | 1800 MPa | |
| bending strength | ISO 178 | 47.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 30.0 MPa |
| flammability | Test Condition | Test Method | AD MAJORIS FRANCE/MAJORIS AG100E |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | AD MAJORIS FRANCE/MAJORIS AG100E |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | 1.1 % | |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 0.60 g/10min |
| Shrinkage rate | TD:2.00mm | 0.90 % | |
| density | ISO 1183 | 1.00 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.20 g/10min |
| 190°C/21.6kg | ISO 1133 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | AD MAJORIS FRANCE/MAJORIS AG100E |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 106 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |