Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 1.3 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| Water absorption rate | | ISO62 | 5.2to5.8 % |
| HumidityAbsorption-62%RH | | ISO1110 | 1.9to2.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Burning rate 4 | | FMVSS302 | <100 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 9500 Mpa |
| Tensile stress | | ISO527-2/5 | 190 Mpa |
| Tensile strain | | ISO527-2/5 | 3.5 % |
| Bending modulus 2 | | ISO178 | 8500 Mpa |
| Bending stress 2 | | ISO178 | 280 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 85 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 255 °C |
| | ISO75-2/C | 210 °C |
| Melting temperature 5 | | DINEN11357-1 | 262 °C |
| | ISO11359-2 | 1.9E-05 cm/cm/°C |
| | ISO11359-2 | 9.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices