Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | Saturation | ASTM D570 | 7.6 % |
| density | | ASTM D792 | 1.22 g/cm³ |
| Shrinkage rate | | ASTM D955 | 1.7 % |
| Water absorption rate | | ASTM D570 | 1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 89.6 MPa |
| elongation | Yield | ASTM D638 | 3.5 % |
| Flexural modulus | | ASTM D790 | 4550 MPa |
| bending strength | Yield | ASTM D790 | 138 MPa |
| compressive strength | | ASTM D695 | 117 MPa |
| shear strength | | ASTM D732 | 62.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 37 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 270 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 22 kV/mm |
| dielectric constant | | ASTM D150 | 4.10 |
| dielectric constant | | ASTM D150 | 1.90 |
| dielectric constant | | ASTM D150 | 3.70 |
| Dissipation Factor | | ASTM D150 | 0.030 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 257 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 249 °C |
| vicat | | ASTM D1525 | 265 °C |
| | ASTM D696 | 4.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.