Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.05 g/cm³ |
| Melt volume flow rate | | ISO1133 | 16.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 56.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 30 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 1.4 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 2.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 48.0 MPa |
| Tensile modulus | | ISO527-2/1 | 2300 MPa |
| Tensile stress | Yield | ISO527-2/50 | 30.0 MPa |
| Tensile stress | Break | ISO527-2/5 | 30.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 5.0 % |
| Tensile strain | Break | ISO527-2/5 | 9.5 % |
| Flexural modulus | | ISO178 | 2790 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 114 °C |
| | ISO75-2/A | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.