Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.09 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 40 g/10min |
| melt mass-flow rate | | ISO1133 | 40 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40to0.70 % |
| density | | ASTMD792 | 1.09 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 95 |
| Rockwell hardness | | ISO2039-2 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 1800 Mpa |
| Tensile modulus | | ISO527-2/50 | 2000 Mpa |
| tensile strength | | ASTMD638 | 43.0 Mpa |
| Tensile stress | | ISO527-2/50 | 43.0 Mpa |
| tensile strength | | ASTMD638 | 26.0 Mpa |
| Tensile stress | | ISO527-2/50 | 31.0 Mpa |
| elongation | | ASTMD638 | 17 % |
| Tensile strain | | ISO527-2/50 | 11 % |
| Flexural modulus | | ASTMD790 | 1700 Mpa |
| Flexural modulus | | ISO178 | 1760 Mpa |
| | ASTMD790 | 49.0 Mpa |
| Bending stress | | ISO178 | 49.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 390 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 200 J/m |
| Suspended wall beam gap impact strength 5 | | ISO180/1A | 40 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 95.0 °C |
| | ISO75-2/B | 85.0 °C |
| | ISO75-2/B | 97.0 °C |
| | ASTMD648 | 80.0 °C |
| | ISO75-2/A | 73.0 °C |
| | ISO75-2/A | 89.0 °C |
| vicat | | ISO306/B50 | 90.0 °C |
| vicat | | ISO306/B120 | 94.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare