PC PANLITE® ML-5202ZLS NA TEIJIN SHANGHAI

Properties:
Light diffusionFlame retardantWeather resistance
Usages:
CastersElectrical applicationsLEDsLighting diffuser
Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	3000μm	ASTM D1003	84.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2400 Mpa
tensile strength	Yield	ISO 527-2/50	65.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	53.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Nominal tensile fracture strain		ISO 527-2/50	25 %
Bending modulus		ISO 178	2350 Mpa
bending strength		ISO 178	97.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	123 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	125 °C
RTI	1.5mm	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.20 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	2.50 cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.