PC ML-5202ZLS NA TEIJIN SHANGHAI
PANLITE®
Casters,Electrical applications,LEDs,Lighting diffuser
Light diffusion,Flame retardant,Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| bending strength | ISO 178 | 97.0 Mpa | |
| Flexural modulus | ISO 178 | 2350 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | 25 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 53.0 Mpa |
| Electrical performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| optical performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 84.0 % |
| flammability | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 3.2mm | UL 94 | 5VA |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 2.50 cm3/10min |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50-0.70 % |
| TD:4.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SHANGHAI/ML-5202ZLS NA |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 125 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 123 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI | 1.5mm | UL 746 | 130 °C |