TPO

TPO PRE-ELEC® PP 1383 Premix Oy

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180	9.0 kJ/m²
Suspended wall beam without notch impact strength	-20°C,4.00mm	ASTM D256	54.6 kJ/m²
	Suspended wall beam without notch impact strength	23°C,4.00mm	ASTM D256	60.9 kJ/m²
		Suspended wall beam without notch impact strength	-20°C	ISO 180	55 kJ/m²
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	59 kJ/m²
Charpy Notched Impact Strength	-20°C	ASTM D256	8.4 kJ/m²
	Charpy Notched Impact Strength	-20°C	ISO 179	9.0 kJ/m²
		Charpy Notched Impact Strength	23°C	ISO 179	12 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ASTM D256	11 kJ/m²
Impact strength of simply supported beam without notch	-20°C	ASTM D256	NoBreak
	Impact strength of simply supported beam without notch	-20°C	ISO 179	NoBreak
		Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ASTM D256	NoBreak
Impact strength of cantilever beam gap	-20°C,4.00mm，Area	ASTM D256	4.20 kJ/m²
	Impact strength of cantilever beam gap	23°C,4.00mm，Area	ASTM D256	8.41 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20°C	ISO 180	5.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	5.0 %
tensile strength		ASTM D638	25.0 MPa
tensile strength	tensile strength		ISO 527-2	25.0 MPa
Tensile strain	Break	ISO 527-2	5.0 %
Bending modulus	4.00mm	ASTM D790	1310 MPa
Bending modulus	Bending modulus	4.00mm	ISO 178	1300 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648B	100 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	100 °C
Vicat softening temperature		ASTM D15253	149 °C
Vicat softening temperature	Vicat softening temperature		ISO 306/A50	150 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/2.16kg	ISO 1133	14 g/10min
Shrinkage rate	MD	ASTM D955	1.2to1.4 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.2to1.4 %
density		ASTM D792	0.996 g/cm³
density	density		ISO 1183	0.990 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	14 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ESDSTM11.11	<1.0E+3 ohms
Surface resistivity	Surface resistivity		IEC 61340-2-3	<1.0E+3 ohms
Volume resistivity		Internal Method	<1.0E+2 ohms·cm

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreA	ASTM D2240	95
	Shore hardness	ShoreD	ASTM D2240	65
		Shore hardness	ShoreA	ISO 868	95
		Shore hardness	Shore hardness	ShoreD	ISO 868	65

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.