TPO PRE-ELEC® PP 1383 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
Charpy Notched Impact Strength | -20°C | ASTM D256 | 8.4 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 9.0 kJ/m² |
Charpy Notched Impact Strength | 23°C | ASTM D256 | 11 kJ/m² |
Impact strength of cantilever beam gap | -20°C | ISO 180 | 5.0 kJ/m² |
Suspended wall beam without notch impact strength | -20°C | ISO 180 | 55 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ASTM D256 | NoBreak |
-20°C | ASTM D256 | NoBreak | |
-20°C | ISO 179 | NoBreak | |
Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180 | 59 kJ/m² |
-20°C,4.00mm | ASTM D256 | 54.6 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
Impact strength of cantilever beam gap | -20°C,4.00mm,Area | ASTM D256 | 4.20 kJ/m² |
23°C,4.00mm,Area | ASTM D256 | 8.41 kJ/m² | |
Suspended wall beam without notch impact strength | 23°C,4.00mm | ASTM D256 | 60.9 kJ/m² |
Charpy Notched Impact Strength | -20°C | ISO 179 | 9.0 kJ/m² |
hardness | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 65 |
邵氏D | ISO 868 | 65 | |
邵氏A | ISO 868 | 95 | |
邵氏A | ASTM D2240 | 95 |
Electrical performance | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
Surface Resistivity | ESDSTM11.11 | <1.0E+3 ohms | |
IEC 61340-2-3 | <1.0E+3 ohms | ||
Volume resistivity | 内部方法 | <1.0E+2 ohms·cm |
Mechanical properties | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 5.0 % |
tensile strength | ASTM D638 | 25.0 MPa | |
ISO 527-2 | 25.0 MPa | ||
Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
Flexural modulus | 4.00mm | ASTM D790 | 1310 MPa |
4.00mm | ISO 178 | 1300 MPa |
physical property | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 1.2to1.4 % |
MD | ISO 294-4 | 1.2to1.4 % | |
melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 14 g/10min |
density | ASTM D792 | 0.996 g/cm³ | |
ISO 1183 | 0.990 g/cm³ | ||
melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 14 g/10min |
Thermal performance | Test Condition | Test Method | Premix Oy/PRE-ELEC® PP 1383 |
---|---|---|---|
vicat | ISO 306/A50 | 150 °C | |
ASTM D15253 | 149 °C | ||
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648B | 100 °C |
0.45MPa,未退火,HDT | ISO 75-2/Bf | 100 °C |