Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.08 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Shrinkage rate | | ISO 294-4 | 1.2to1.4 % |
| Shrinkage rate | | ISO 294-4 | 1.2to1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore) | | ASTM D2240 | 65 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 2.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 25.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 5.0 % |
| Flexural modulus | | ISO 178 | 2000 MPa |
| bending strength | | ISO 178 | 45.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 108 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 62.0 °C |
| vicat | | ISO 306/A50 | 154 °C |
| vicat | | ISO 306/B50 | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.