Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Homopolymer POLYfill PPH 150DNH 瑞典柏力开米
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
| -20°C | ISO 179 | 2.0 kJ/m² |
| hardness | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Hardness (Shore) | 邵氏D,15秒 | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2000 MPa |
| tensile strength | ISO 527-2 | 25.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| bending strength | ISO 178 | 45.0 MPa |
| flammability | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Hot filament ignition temperature | 1.6mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.2to1.4 % |
| MD | ISO 294-4 | 1.2to1.4 % | |
| density | ISO 1183 | 1.08 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | 瑞典柏力开米/POLYfill PPH 150DNH |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 62.0 °C |
| vicat | -- | ISO 306/A50 | 154 °C |
| -- | ISO 306/B50 | 99.0 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 108 °C |
Contact Us
Get App