Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| humidity | | ISO 1110 | 0.20 % |
| ash content | | 内部方法 | 25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 79 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Tensile modulus | | ISO 527-2 | 8000 MPa |
| tensile strength | | ISO 527-2 | 143 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 43 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| dielectric strength | | IEC 60243-1 | 40 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 200 °C |
| vicat | | ISO 306 | >200 °C |
| Heat distortion temperature | | ISO 75-2/B | 215 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.