PA6 BESTNYL SI25VI01A TRIESA SPAIN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 43 kJ/m² |
| hardness | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 79 |
| Electrical performance | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 40 kV/mm | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| Mechanical properties | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| tensile strength | ISO 527-2 | 143 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Tensile modulus | ISO 527-2 | 8000 MPa |
| flammability | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| humidity | 颗粒 | ISO 1110 | 0.20 % |
| Shrinkage rate | ISO 294-4 | 0.30 % | |
| ash content | 内部方法 | 25 % | |
| density | ISO 1183 | 1.30 g/cm³ |
| Thermal performance | Test Condition | Test Method | TRIESA SPAIN/BESTNYL SI25VI01A |
|---|---|---|---|
| vicat | ISO 306 | >200 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |