Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.10 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | | 90000 cP |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| electric strength | | | 22 kV/mm |
| | | 6.40 |
| Volume resistivity | | | 4.9E+16 ohms·cm |
| Dissipation Factor | | | 0.018 |
| Water absorption rate | | | 0.11 % |
| Supporting hardness | | | 95 |
| Tensile modulus | | | 10300 MPa |
| tensile strength | | | 58.6 MPa |
| Compression Strength | | | 117 MPa |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| MixRatiobyWeight(PBW) | | | 100 |
| MixRatiobyWeight(PBW) | | | 3.0到4.0 |
| MixRatiobyWeight(PBW) | | | 2.29 g/cm³ |
| MixRatiobyWeight(PBW) | | | 2.0 hr |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Operating | | | -55.0到205 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | | 93.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 19 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 3E-05 cm/cm/°C |
| thermal conductivity | | | 1.7 W/m/K |
| | | 175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.