Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.10 - 0.40 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 13000 Mpa |
| tensile strength | | ISO 527-2 | 230 Mpa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 11000 Mpa |
| bending strength | | ISO 178 | 320 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180 | 40 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D2520 | 3.50 |
| Dissipation Factor | | ASTM D2520 | 0.010 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 0.50 to 1.5 hr |
| Temperature at the rear of the barrel | | | 250 to 260 °C |
| Temperature at the front of the material cylinder | | | 260 to 290 °C |
| Processing (melt) temperature | | | 280 to 300 °C |
| Temperature | | | 120 to 140 °C |
| injection speed | | | 快速 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices