PARA 1038 BK000 SOLVAY USA
IXEF®
Automotive interior parts、sporting goods
high strength、Creep resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 13000 Mpa | |
| bending strength | ISO 178 | 320 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 11000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 230 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| Dissipation Factor | 2.40 GHz | ASTM D2520 | 0.010 |
| dielectric constant | 2.40 GHz | ASTM D2520 | 3.50 |
| physical property | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| Shrinkage rate | 流量 | 内部方法 | 0.10 - 0.40 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 230 °C |
| injection | Test Condition | Test Method | SOLVAY USA/1038 BK000 |
|---|---|---|---|
| drying time | 0.50 to 1.5 hr | ||
| Temperature at the rear of the barrel | 250 to 260 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 260 to 290 °C | ||
| Temperature | 120 to 140 °C | ||
| injection speed | 快速 |