Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10 min |
| density | | ASTM D792 | 1.15 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70.0 °C |
| drying time | | | 1.0 to 2.0 hr |
| Barrel Temperature | | | 160 to 200 °C |
| Barrel Temperature | | | 180 to 220 °C |
| Barrel Temperature | | | 200 to 240 °C |
| Barrel Temperature | | | 200 to 240 °C |
| die temperature | | | 190 to 220 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 23.5 MPa |
| elongation | Break | ASTM D638 | 40 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
| injection | Test Condition | Test Method | Test Result |
|---|
| Temperature in the middle of the barrel | | | 190 to 220 °C |
| Temperature at the front of the material cylinder | | | 210 to 240 °C |
| Spray nozzle temperature | | | 200 to 230 °C |
| Temperature | | | 40.0 to 60.0 °C |
| drying temperature | | | 70.0 °C |
| drying time | | | 1.0 to 2.0 hr |
| Temperature at the rear of the barrel | | | 180 to 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.