Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 12.0 cm³/10min |
| Shrinkage rate | | 内部方法 | 0.70到0.80 % |
| Water absorption rate | | ASTMD570 | 0.16 % |
| Water absorption rate | | ISO62 | 0.16 % |
| density | | ASTMD792,ISO1183 | 1.20 g/cm³ |
| density | | ASTMD792 | 1.19 g/cm³ |
| Specific volume | | ASTMD792 | 0.830 cm³/g |
| melt mass-flow rate | | ASTMD1238 | 3.0 g/10min |
| Melt volume flow rate | | ISO1133 | 3.00 cm³/10min |
| Water absorption rate | | ISO62 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 122 |
| Rockwell hardness | M-Scale | ASTMD785 | 85 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.600 |
| transmissivity | | ASTMD1003 | 85.0 % |
| Haze ratio | | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO527-2/50 | >50 % |
| Flexural modulus | | ASTMD790 | 2030 MPa |
| Flexural modulus | | ISO178 | 2130 MPa |
| Bending stress | | ISO178 | 66.0 MPa |
| Bending stress | | ASTMD790 | 95.1 MPa |
| Tensile modulus | | ASTMD638 | 2090 MPa |
| Tensile modulus | | ISO527-2/1 | 2260 MPa |
| tensile strength | | ASTMD638 | 65.5 MPa |
| tensile strength | Yield | ISO527-2/5,ISO527-2/50 | 65.0 MPa |
| tensile strength | | ASTMD638 | 71.7 MPa |
| tensile strength | Break | ISO527-2/50 | 65.0 MPa |
| elongation | | ASTMD638 | 7.0 % |
| elongation | Yield | ISO527-2/50 | 7.0 % |
| elongation | | ASTMD638 | 120 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 140 J/m |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 73.0 J |
| Falling hammer impact | | ASTMD3029 | 149 J |
| Impact strength of cantilever beam gap | | ASTMD256 | 640 J/m |
| Impact strength of cantilever beam gap | | ISO180/1A | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 13 kJ/m² |
| Tensile impact strength | | ASTMD1822 | 578 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD4812 | 3200 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >2.6E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| dielectric constant | | ASTMD150 | 3.15 |
| dielectric constant | | ASTMD150 | 3.15 |
| dielectric constant | | ASTMD150 | 3.00 |
| Dissipation Factor | | ASTMD150 | 1.2E-03 |
| Dissipation Factor | | ASTMD150 | 1.2E-03 |
| Dissipation Factor | | ASTMD150 | 0.024 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| High arc combustion index (HAI) | | UL746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTME831 | 9.2E-05 cm/cm/°C |
| | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.21 W/m/K |
| RTI Elec | | UL746 | 125 °C |
| RTI Imp | | UL746 | 125 °C |
| RTI | | UL746 | 125 °C |
| | ASTMD648 | 143 °C |
| | ISO75-2/Af | 132 °C |
| vicat | | ASTMD152511 | 160 °C |
| vicat | | ISO306/B50 | 154 °C |
| vicat | | ISO306/B120 | 155 °C |
| | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare