PPC LEXAN™ HPH4504HEU resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
Charpy Notched Impact Strength23°CISO 179/1eA15 kJ/m²
Impact strength of cantilever beam gap-30°C8ISO 180/1A11 kJ/m²
-30°CASTM D256140 J/m
Dart impact23°C,TotalEnergyASTM D376373.0 J
Impact strength of cantilever beam gap23°CASTM D256640 J/m
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
Impact strength of cantilever beam gap23°C8ISO 180/1A13 kJ/m²
ASTM D1822578 kJ/m²
Dart impact23°CASTM D3029149 J
hardnessTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
Rockwell hardnessM级ASTM D78585
R级ASTM D785122
Mechanical propertiesTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
tensile strength 屈服3ASTM D63865.5 MPa
屈服ISO 527-2/565.0 MPa
elongation断裂3ASTM D638120 %
断裂ISO 527-2/50>50 %
Flexural modulus--5ISO 1782130 MPa
Tensile modulus--ISO 527-2/12260 MPa
bending strength屈服,50.0mm跨距4ASTM D79095.1 MPa
Flexural modulus50.0mm跨距4ASTM D7902030 MPa
bending strength--5,6ISO 17866.0 MPa
elongation屈服ISO 527-2/507.0 %
屈服3ASTM D6387.0 %
tensile strength 断裂3ASTM D63871.7 MPa
Tensile modulus--2ASTM D6382090 MPa
tensile strength 断裂ISO 527-2/5065.0 MPa
Electrical performanceTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
dielectric strength3.20mm,inAirASTM D14920 kV/mm
Dissipation Factor50HzASTM D1501.2E-03
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 3
Dissipation Factor60HzASTM D1501.2E-03
dielectric constant60HzASTM D1503.15
Volume resistivityASTM D257>2.6E+17 ohms·cm
dielectric constant50HzASTM D1503.15
Dissipation Factor100HzASTM D1500.024
High arc combustion index (HAI)HAIUL 746PLC 4
Hot wire ignition (HWI)HWIUL 746PLC 2
dielectric constant1MHzASTM D1503.00
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
optical performance Test ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
Haze ratio2540µmASTM D10031.0 %
refractive indexASTM D5421.600
transmissivity2540µmASTM D100385.0 %
flammabilityTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
UL flame retardant rating1.5mmUL 94V-2
physical property Test ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
Melt volume flow rate330°C/2.16kgISO 113312.0 cm³/10min
Shrinkage rateMD：3.20mm内部方法0.70to0.80 %
Water absorption rate24hrASTM D5700.16 %
平衡,23°C,50%RHISO 620.35 %
饱和,23°CISO 620.16 %
density--ASTM D7921.19 g/cm³
Melt volume flow rate300°C/1.2kgISO 11333.00 cm³/10min
Specific volumeASTM D7920.830 cm³/g
density--ASTMD7921.20 g/cm³
melt mass-flow rate300°C/1.2kgASTM D12383.0 g/10min
Thermal performanceTest ConditionTest MethodSABIC/LEXAN™ HPH4504HEU resin
vicat--ASTM D152511160 °C
Linear coefficient of thermal expansionMD:-40到95°CASTME8319.2E-05 cm/cm/°C
RTIUL 746125 °C
specific heatASTMC3511260 J/kg/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距10，HDTISO 75-2/Af132 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8316E-05 cm/cm/°C
vicat--ISO 306/B120155 °C
thermal conductivityASTMC1770.21 W/m/K
Linear coefficient of thermal expansionTD:-40到40°CASTME8316E-05 cm/cm/°C
vicat--ISO 306/B50154 °C
RTI ImpUL 746125 °C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648143 °C
RTI ElecUL 746125 °C