Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.13 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Water absorption rate | | ASTM D570 | 0.35 % |
| intrinsic viscosity | | 内部方法 | 1.1 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 95 |
| Shore hardness | | ASTM D2240 | 55 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D1004 | 370 N |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | 300 % |
| Flexural modulus | | ASTM D790 | 150 MPa |
| coefficient of friction | | ASTM D1894 | >1.0 |
| Tensile modulus | | ASTM D638 | 170 MPa |
| tensile strength | | ASTM D638 | 14.0 MPa |
| tensile strength | | ASTM D638 | 20.0 MPa |
| elongation | | ASTM D638 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 50 J/m |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Kappa modulus | | ASTM D1043 | 930 MPa |
| Kappa modulus | | ASTM D1043 | 240 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D882 | 26 % |
| elongation | | ASTM D882 | 26 % |
| elongation | | ASTM D882 | 550 % |
| elongation | | ASTM D882 | 550 % |
| OTr | | ASTM D1434 | 841 cm³/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF372 | 130 g/m²/24hr |
| film thickness | | | 130 µm |
| Secant modulus | | ASTM D882 | 185 MPa |
| Secant modulus | | ASTM D882 | 179 MPa |
| tensile strength | | ASTM D882 | 13.7 MPa |
| tensile strength | | ASTM D882 | 13.5 MPa |
| tensile strength | | ASTM D882 | 23.7 MPa |
| tensile strength | | ASTM D882 | 22.6 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | DSC | 2000 J/kg/°C |
| specific heat | | DSC | 2300 J/kg/°C |
| specific heat | | DSC | 3100 J/kg/°C |
| Glass Transition Temperature | | DSC | -3.00 °C |
| vicat | | ASTM D15256 | 170 °C |
| brittle temperature | | ASTM D746 | <-75.0 °C |
| specific heat | | DSC | 2300 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.19 W/m/K |
| Fusion temperature | | ASTME793 | 27.0 kJ/kg |
| melting temperature | | ASTM D3418 | 207 °C |
| Crystallization peak temperature | | DSC | 140 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.5E-04 cm/cm/°C |
| specific heat | | DSC | 1600 J/kg/°C |
| specific heat | | DSC | 1800 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.