Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 1.0 -- |
| Water absorption rate | | % | 0.75 -- |
| density | | g/cm³ | 1.19 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 105 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | MPa | 82.0 -- |
| tensile strength | | MPa | 67.0 54.0 |
| elongation | Break | % | 15 22 |
| Flexural modulus | | MPa | 2600 1100 |
| bending strength | | MPa | 100 78.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 54 150 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | -- 1E+14 |
| dielectric strength | | kV/mm | -- 25 |
| dielectric constant | | | -- 3.60 |
| Dissipation Factor | | | -- 0.040 |
| arc resistance | | sec | -- 80.0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 150 -- |
| | cm/cm/°C | 7.4E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare