Polyarylate U-polymer AXF-1500-05 UNITIKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.18mm | J/m | 54 150 |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| Rockwell hardness | R级 | 105 -- |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| compressive strength | MPa | 82.0 -- | |
| bending strength | MPa | 100 78.0 | |
| elongation | 断裂 | % | 15 22 |
| Flexural modulus | MPa | 2600 1100 | |
| tensile strength | MPa | 67.0 54.0 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| arc resistance | sec | 80.0 -- | |
| Volume resistivity | ohms·cm | -- 1E+14 | |
| dielectric constant | 1MHz | 3.60 -- | |
| dielectric strength | kV/mm | 25 -- | |
| Dissipation Factor | 1MHz | 0.040 -- |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | % | 1.0 -- |
| density | g/cm³ | 1.19 -- | |
| Water absorption rate | 24hr,3.18mm | % | 0.75 -- |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AXF-1500-05 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 7.4E-05 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 150 -- |