ABS Novodur® HH-112 BK10009
168
- Properties:heat-resistingHigh rigidity
- Usages:Automotive interior partsAutomotive sectorAutomotive External PartsApplication in the automotive field
Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
melt mass-flow rate | ASTM D1238 | 6.0 g/10min | |
Melt volume flow rate | ISO 1133 | 6.00 cm3/10min | |
Shrinkage rate | ASTM D955 | 0.55 % | |
ISO 294-4 | 0.40-0.70 % | ||
Water absorption rate | ISO 62 | 0.25 % | |
ASTM D570 | 0.3 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Flexural modulus | ASTM D790 | 2700 Mpa | |
ISO 178 | 2700 Mpa | ||
bending strength | ASTM D790 | 88.3 Mpa | |
ISO 178 | 81.0 Mpa | ||
Tensile modulus | ASTM D638 | 2800 Mpa | |
ISO 527-2 | 2700 Mpa | ||
tensile strength | ASTM D638 | 58.0 Mpa | |
ISO 527-2 | 58.0 Mpa | ||
Tensile strain | ISO 527-2 | 3.1 % | |
elongation | ASTM D638 | 3.0 % | |
Nominal tensile fracture strain | ISO 527-2 | 8.0 % | |
ball-indentation hardness | ISO 2039-1 | 114 Mpa | |
tensile strength | ISO 527-2 | 580 kg/cm | |
ISO 527-2 | 390 kg/cm | ||
elongation | ISO 527-2 | 3.0 % | |
ISO 527-2 | 20 % | ||
Tensile modulus | ISO 527-2 | 28000 kg/cm | |
bending strength | ISO 178 | 880 kg/cm | |
Flexural modulus | ISO 178 | 27000 kg/cm | |
Rockwell hardness | 115 R |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179 | 80 kJ/m² | |
ISO 179 | 140 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
dielectric strength | IEC 60243-1 | 41 KV/mm | |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
IEC 60093 | 1E+15 ohms·cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Heat distortion temperature | ISO 75-2/B | 110 °C | |
ISO 75-2/A | 102 °C | ||
vicat | ISO 306/A50 | 118 °C | |
ISO 306/B50 | 112 °C | ||
Linear coefficient of thermal expansion | ISO 11359-2 | 9E-05 cm/cm/°C | |
thermal conductivity | DIN 52612 | 0.17 W/m/K | |
maximum service temperature | 90 °C | ||
vicat | ISO 306 | 112 °C | |
Heat distortion temperature | ASTM D648 | 109 °C | |
UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.