ABS HH-112 BK10009 INEOS STYRO KOREA
Novodur®
Automotive interior parts、Automotive sector、Automotive External Parts、Application in the automo
heat-resisting、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | INEOS STYRO KOREA/HH-112 BK10009 |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179 | 80 kJ/m² |
23°C | ISO 179 | 140 kJ/m² |
Electrical performance | Test Condition | Test Method | INEOS STYRO KOREA/HH-112 BK10009 |
---|---|---|---|
Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
IEC 60093 | 1E+15 ohms·cm | ||
dielectric strength | 1.50mm | IEC 60243-1 | 41 KV/mm |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
Mechanical properties | Test Condition | Test Method | INEOS STYRO KOREA/HH-112 BK10009 |
---|---|---|---|
Rockwell hardness | 115 R | ||
Tensile modulus | ISO 527-2 | 2700 Mpa | |
bending strength | ISO 178 | 880 kg/cm | |
ASTM D790 | 88.3 Mpa | ||
ball-indentation hardness | ISO 2039-1 | 114 Mpa | |
tensile strength | 屈服 | ISO 527-2 | 580 kg/cm |
屈服,23°C | ASTM D638 | 58.0 Mpa | |
Flexural modulus | ASTM D790 | 2700 Mpa | |
Tensile modulus | ASTM D638 | 2800 Mpa | |
elongation | 屈服 | ISO 527-2 | 3.0 % |
断裂 | ASTM D638 | 3.0 % | |
bending strength | ISO 178 | 81.0 Mpa | |
Flexural modulus | ISO 178 | 2700 Mpa | |
tensile strength | 屈服,23°C | ISO 527-2 | 58.0 Mpa |
Tensile strain | 屈服,23°C | ISO 527-2 | 3.1 % |
tensile strength | 断裂 | ISO 527-2 | 390 kg/cm |
Tensile modulus | ISO 527-2 | 28000 kg/cm | |
Nominal tensile fracture strain | 23°C | ISO 527-2 | 8.0 % |
elongation | 断裂 | ISO 527-2 | 20 % |
Flexural modulus | ISO 178 | 27000 kg/cm |
physical property | Test Condition | Test Method | INEOS STYRO KOREA/HH-112 BK10009 |
---|---|---|---|
Shrinkage rate | MD | ASTM D955 | 0.55 % |
ISO 294-4 | 0.40-0.70 % | ||
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.25 % |
melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 6.0 g/10min |
Water absorption rate | ASTM D570 | 0.3 % | |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 6.00 cm3/10min |
Thermal performance | Test Condition | Test Method | INEOS STYRO KOREA/HH-112 BK10009 |
---|---|---|---|
thermal conductivity | DIN 52612 | 0.17 W/m/K | |
vicat | ISO 306 | 112 °C | |
-- | ISO 306/A50 | 118 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 102 °C |
vicat | -- | ISO 306/B50 | 112 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,Annealed,HDT | ISO 75-2/B | 110 °C |
1.8Mpa,HDT | ASTM D648 | 109 °C | |
maximum service temperature | 90 °C | ||
UL flame retardant rating | UL 94 | HB |